| description: | Applications:
HYBRAKE: Car, MPV, Light Heavy-Duty Vehicle, Motorcycle & Other Vehicle.
Features:
HYBRAKE: Low expansion, resistance to high temperature, ozone, low moisture permeation, whip and impulse.
Standard：
SAE J1401,SAE J1402,GB16897-97, FMVSS 106
Technical Data
Test Items |
Test Condition |
Standard Spec |
Test Results |
|
ID |
|
3.2mm |
3.15～3.45 |
|
OD |
|
10.5mm |
10.30～10.70 |
|
Volumetric expansion |
6.9MPa |
1.08ml/m |
0.562ml/m |
|
10.3MPa |
1.38ml/m |
0.783ml/m |
|
Burst |
27.6MPa × 2min； pressure raste 172.5±69MPa/min |
no leakage，＞49MPa |
＞75MPa |
|
Brake fluid compatibilit |
120℃ × 70h，27.6MPa × 2min；pressure raste 172.5±69MPa/min |
no leakage，＞49MPa |
＞80MPa |
|
Whip |
keep 1.55～1.72MPa |
＞35h |
＞80h |
|
Tensile |
tensile speed：25±3mm/min |
＞1446N |
2400N |
|
Cold Bend |
-45℃ ～-48℃× 72h， 3-5s,bending180° |
no crack,no rupture |
no crack,no rupture |
|
Ozone |
100pphm×70h×40℃， enlarge 7 times |
no cracking |
no cracking |
|
Salt Spray |
5%NaCl,after24h，water cleanout in 35℃ |
no recl rust on fitting |
no recl rust on fitting |
|
Water Aging |
putat water in 85±2℃,after 70h～72h 27.6MPa × 2min；pressure raste 172.5±69MPa/min |
burst＞49h； whip＞35h； tensile≥1446N |
＞82MPa； ＞60h； ＞2500N |
|